MATERIAL:
BS 1407 C= 1.1 Si= 0.22 Mn= 0.37 Cr= 0.43 P= < 0.45 S= < 0.45 1.2210, 115 Cr V3 C=1.10 ÷1.25 Si= 0.15 ÷ 0.30 Mn= 0.20 ÷ 0.40 Cr= 0.50 ÷ 0.80 V= 0.07 ÷ 0.12 P= < 0.03 S= < 0.03 |
LENGHT:
1000 mm
Example of designation: CSS 3 x 1000 |
|
|
Supplied: annealed
Hardeness HB 207-237
Tensile strenght 700 / 850 N/mm2
DIAMETER TOLERANCE
> 25 mm +0 / 0,015
< 25 mm +0 / 0,025
MATERIAL: BS 1407 o 1.2210, 115 Cr V3 according to stock availability
SURFACE FINISH
Roughness < 0,6 micron
THERMAL TREATMENT:
Hardening
In case of low carbon level, heat slowly up to 760-800 °C.
In case of high carbon level, maintain on minimum temperature. Leave the temperature uniforms. Then harden in well stirred (agited) water. Hardness reached after hardening: about 65-68 hrc. The approximate quench hardness is 65 to 68 Rc.
TEMPERING
Proceed with temperatures between 180 °C and 350 °C according to the usage needs and referring to the tempering curve (see below).
PACKAGING
Bars are protected from corrosion by applying a solution of lanolin.
In addition, all bars are carefully packed to prevent damage during handling and transport.
APPLICATIONS
Gauges, spindles, pins, various tools, punches, points, moulds accessories, e.t.c.